- Total Solid Content (TSC) %: 58.0
- Mechanical Stability (secs): 1000 min
- Ammonia content (%): 0.68
- Ford Cup 3 Viscosity @ 25°C (sec): 30.0
- pH: 10.8
- Unaged modulus at 700% (MPa): 9.0
- Unaged tensile strenght (MPa): 28.0
- Unaged elongation at Break (%): 950
- Aged (22hrs at 100ºC ) modulus at 700% (MPa): 50 min
- Aged (22hrs at 100ºC ) tensile strenght: 75 Average results
- Product form(s): Liquid
- Packaging option(s): Bulk
PVL8006
About PVL8006
High ammonia PV NRL low modulus (PVL8006) is a high ammonia prevulcanised natural rubber latex having a low modulus with high purity/low toxicity rating making it an ideal latex for the production of medical goods.
Product Data Sheet 
Product Data Sheet
PVL8006
Date: Sunday, Dec 10, 2023
Product Specification
| Total Solid Content (TSC) % | 58.0 |
| Mechanical Stability (secs) | 1000 min |
| Ammonia content (%) | 0.68 |
| Ford Cup 3 Viscosity @ 25°C (sec) | 30.0 |
| pH | 10.8 |
| Unaged modulus at 700% (MPa) | 9.0 |
| Unaged tensile strenght (MPa) | 28.0 |
| Unaged elongation at Break (%) | 950 |
| Aged (22hrs at 100ºC ) modulus at 700% (MPa) | 50 min |
| Aged (22hrs at 100ºC ) tensile strenght | 75 Average results |
| Product form(s): | Liquid |
| Packaging option(s) | Bulk |